On the mechanical behavior of BFRP to aluminum AA6086 mixed joints
2013
The aim of this work is to analyze the possibility to join aluminum alloy AA6086 and composite laminates reinforced with basalt fibers, an innovative material which use is growing in several applications as an alternative to glass fibers. To this goal, three joining techniques were investigated: mechanical by Self Piercing Riveting (in the next called SPR), adhesive by co-curing technique and mixed in which the joining techniques (i.e. adhesive and mechanical) were combined. Two manufacturing technologies (i.e. hand lay-up and vacuum bagging) were used both to produce composite substrates and to realize co-curing adhesion between the substrates to be joined. Mixed joints were realized by in…
Bilayer biodegradable films prepared by co-extrusion film blowing: Mechanical performance, release kinetics of an antimicrobial agent and hydrolytic …
2020
Abstract Bilayer biodegradable, eco-friendly films were prepared by co-extrusion film blowing, coupling polylactic acid (PLA) and Bio-flex ® (BIO). Furthermore, in the PLA layer, carvacrol (CRV) was added as a natural antimicrobial additive, whereas a nanoclay (D72T) was integrated to protect CRV from volatilization and to modulate release. The materials were analyzed by morphological, chemical-physical, mechanical testing. Furthermore, CRV release and degradation tests were performed. The results pointed out that coupling the two matrices allows gathering the stiffness of PLA with the ductility of BIO. Furthermore, the interlayer adhesion is promoted by CRV. D72T exerts a key-role in avoid…
On the response of flax fiber reinforced composites under salt-fog/dry conditions: Reversible and irreversible performances degradation
2022
Abstract Despite their scarce resistance to humid or wet conditions, natural fiber reinforced composites (NFRCs) seem to be able to partially recover their performances under discontinuous exposition to marine environment. To investigate this peculiarity, flax fiber reinforced composite was at first subjected to salt-fog spray condition at 35 °C for 15 and 30 days, respectively, and then stored in ‘‘dry” condition (i.e., 50% R.H. and 22 °C) between 0 and 21 days. The performances evolution was evaluated through flexural tests, water uptake and contact angle measurements. Moreover, the morphology of fractured mechanical samples was examined by using 3D optical microscope and scanning electro…
Mechanical Behavior of Steel Fiber-Reinforced Concrete Beams Bonded with External Carbon Fiber Sheets
2017
This study investigates the mechanical behavior of steel fiber-reinforced concrete (SFRC) beams internally reinforced with steel bars and externally bonded with carbon fiber-reinforced polymer (CFRP) sheets fixed by adhesive and hybrid jointing techniques. In particular, attention is paid to the load resistance and failure modes of composite beams. The steel fibers were used to avoiding the rip-off failure of the concrete cover. The CFRP sheets were fixed to the concrete surface by epoxy adhesive as well as combined with various configurations of small-diameter steel pins for mechanical fastening to form a hybrid connection. Such hybrid jointing techniques were found to be particularly adva…
Concrete columns confined with fibre reinforced cementitious mortars: Experimentation and modelling
2014
Abstract The structural behaviour of concrete columns strengthened with a system made up of fibre nets embedded in an inorganic stabilized cementitious matrix under an uniaxial load was investigated. Medium size specimens with circular and square cross-section were cast and subjected to monotonic uniaxial compression, to investigate the efficiency of a p-Phenylene BenzobisOxazole (PBO) Fibre Reinforced Cementitious Mortar (FRCM) system in increasing both strength and ductility. The experimental results show that the confinement system adopted produced a noticeable increment in strength and ductility, though the low mechanical ratios of fibre considered were not always able to ensure hardeni…
Bond characterization of monolithic and layered glass panels and ultrasonic tests to control glued surfaces
2019
Abstract An experimental investigation is presented regarding the compressive and shear strength of monolithic and PVB laminated glass elements connected by acrylic glue. Ultrasonic tests were also used to control the efficiency of glued surfaces of glass panels. Twenty-four triplets composed of three float glass elements glued with acrylic adhesive were prepared to perform bond tests. Of these twelve triplets were made with monolithic glass elements with a nominal thickness of 20 mm, while twelve were made with layered glass elements 20 mm thick. Three single elements of monolithic glass and three of layered glass were tested for compressive strength. Ultrasonic tests were performed on a s…
Bending test for capturing the vivid behavior of giant reeds, returned through a proper fractional visco-elastic model
2015
Abstract This paper presents results of experimental investigations made to evaluate the vivid behavior of giant reed Arundo donax. In particular, attention was paid to the relationship between visco-elastic properties and moisture content, which is widely recognized as one of the key factor that influences the mechanical properties of all wood-based materials. To this aim, after a controlled drying treatment on samples of reed, stress relaxation tests in three point bending configuration were performed to evaluate the effects of moisture content on visco-elastic behavior of the giant reed. Further, the novel aspect of this paper is that of using an Euler–Bernoulli model embedded with an ad…
The effect of alkaline treatment on mechanical properties of kenaf fibers and their epoxy composites
2015
Abstract In this work, kenaf fibers were pre-treated in a NaOH solution (6% in weight) at room temperature for two different periods (48 and 144 h). The chemical treatment of kenaf fibers for 48 h allowed to clean their surface removing each impurity whereas 144 h of immersion time had detrimental effect on the fibers surface and, consequently, on their mechanical properties. Untreated and NaOH treated kenaf fibers (i.e. for 48 h) were also used as reinforcing agent of epoxy resin composites. The effect of the stacking sequence (i.e. using unidirectional long fibers or randomly oriented short fibers) and the chemical treatment on the static mechanical properties was evaluated showing that t…
Assessment of performance degradation of hybrid flax-glass fiber reinforced epoxy composites during a salt spray fog/dry aging cycle
2022
The main goal of this paper is the evaluation of the performances reversibility of hybrid composites when they are dried after being aged in salt-fog environment. To this aim, epoxy composites reinforced with flax and glass fabrics respectively in the internal and external laminae were at first exposed to salt-fog (i.e., identified as wet phase) and then stored in controlled conditions (i.e., identified as dry phase). The flexural properties evolution of these composites as well as their water uptake and contact angle were monitored at varying time of both phases. The flexural strength and modulus of hybrid composites is 23.4% (17.9%) and 15.5% (12.9%) lower than unaged ones after 30 (15) d…